PC
L1225Y
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
吸水率 |
24hr ， in 23 ℃ |
ASTM D-570 |
0.2 |
% |
| 物理性能 |
透光率 |
厚度 3mm |
ASTM D-1003 |
88 |
% |
| 折射率 |
--- |
ASTM D-542 |
1.585 |
--- |
| 阻燃性 |
厚度 1.47mm |
UL 94 |
94V-2 |
--- |
| 阻燃性 |
厚度 3.05mm |
UL 94 |
94V-2 |
--- |
| 比重 |
--- |
ASTM D-792 |
1.2 |
--- |
| 机械性能 |
拉伸强度 |
屈服点 |
--- |
ASTM D-638 |
62(630) |
Mpa(kgf/cm 2 ) |
| 断裂点 |
|
78(800) |
|
| 拉伸模量 |
--- |
ASTM D-638 |
2130(21700) |
Mpa(kgf/cm 2 ) |
| 拉伸率 |
屈服点 |
--- |
ASTM D-638 |
6 |
--- |
| 断裂点 |
|
140 |
| 弯曲强度 |
--- |
ASTM D-790 |
90(920) |
Mpa(kgf/cm 2 ) |
| 弯曲模量 |
--- |
ASTM D-792 |
2260(23000) |
Mpa(kgf/cm 2 ) |
| 压缩强度 |
--- |
ASTM D-695 |
76(780) |
Mpa(kgf/cm 2 ) |
| 耐冲击强度值 |
艾氏、带缺口厚度 3.2mm |
ASTM D-256 |
830(85) |
j/m(kgf·cm/cm) |
| 耐冲击强度值 |
艾氏、带缺口厚度 6.4mm |
ASTM D-256 |
130(13) |
j/m(kgf·cm/cm) |
| 洛氏硬度 |
--- |
ASTM D-785 |
77 |
洛氏硬度 |
| 电气性能 |
绝缘破坏强度 |
快速加压值厚度 1.6mm |
ASTM D-149 |
30 |
KV/mm |
| 体积电阻率 |
--- |
ASTM D-257 |
3 |
10 16 Ω .cm |
| 介电率 |
60Hz |
ASTM D-150 |
2.95 |
--- |
| 介电率 |
10 6 Hz |
ASTM D-150 |
2.9 |
--- |
| 介电正切 |
60Hz |
ASTM D-150 |
0.0004 |
--- |
| 介电正切 |
10 6 Hz |
ASTM D-150 |
0.009 |
--- |
| 耐电弧性 |
--- |
ASTM D-495 |
110 |
sec |
| 耐导电径迹性（ CTI ） |
--- |
IEC 112 |
300 |
V |
| 加工性能 |
成型收缩率 |
流动方向 |
--- |
ASTM D-955 |
0.5 ～ 0.7 |
% |
| 垂直方向 |
|
|
|
| 热 性 能 |
负荷挠曲温度 |
负荷 0.451MPa(4.6kgf/cm) |
ASTM D-648 |
142 |
°C |
| 负荷挠曲温度 |
负荷 1.813MPa(18.6kgf/cm) |
ASTM D-648 |
132 |
°C |
| 线膨胀系数 |
流动方向 |
--- |
ASTM D-696 |
7 |
10 -5 cm/cm/ ℃ |
| 垂直方向 |
|
|
|
| 温度指数 |
电学式 |
厚度 1.47mm |
UL 746B |
125 |
°C |
| 冲击式 |
|
|
115 |
|
| 非冲击式 |
|
|
125 |
|
| 用途概述： |
对流动性要求较高的薄壁制品、电器、电子元件、机械零件、劳保
· 医疗用品、照明器具及灯罩、餐具、容器。 |
| 备注说明： |
最适宜于采用注坯吹塑成型。 |
|